Klooritud polüetüleen Magnetic Products jaoks
Üksus | Üksus | Tüüp | ||||
CPE3615G | CM2500A | CM2500B | CPE230A | CPE230B | ||
Kloori sisaldus | % | 36±2 | 25±2 | 25±2 | 30±2 | 30±2 |
Fusioonisoojus | J/g | ≤5,0 | ≤10,0 | ≤2,0 | ≤2,0 | ≤2,0 |
Shore'i kõvadus | A | ≤60 | ≤80 | ≤80 | ≤70 | ≤67 |
Tõmbetugevus | Mpa | ≥8,0 | ≥8,0 | ≥8,0 | ≥8,0 | ≥8,0 |
Break'i pikenemine | % | ≥800 | ≥ 600 | ≥ 600 | ≥800 | ≥800 |
Muutuv sisu | % | ≤0,40 | ≤0,40 | ≤0,40 | ≤0,40 | ≤0,40 |
Mooney viskoossus | ML125℃ 1+4 | 80-90 | 76-82 | 64-70 | 80-90 | 60-70 |
Märkus. Palun kinnitage meiega, kui teil on erinõudeid. |
Üksus | Üksus | Tüüp | ||||
CPE3615G | CM2500A | CM2500B | CPE230A | CPE230B | ||
Kloori sisaldus | % | 36±2 | 25±2 | 25±2 | 30±2 | 30±2 |
Fusioonisoojus | J/g | ≤5,0 | ≤10,0 | ≤2,0 | ≤2,0 | ≤2,0 |
Shore'i kõvadus | A | ≤60 | ≤80 | ≤80 | ≤70 | ≤67 |
Tõmbetugevus | Mpa | ≥8,0 | ≥8,0 | ≥8,0 | ≥8,0 | ≥8,0 |
Break'i pikenemine | % | ≥800 | ≥ 600 | ≥ 600 | ≥800 | ≥800 |
Muutuv sisu | % | ≤0,40 | ≤0,40 | ≤0,40 | ≤0,40 | ≤0,40 |
Mooney viskoossus | ML125℃ 1+4 | 80-90 | 76-82 | 64-70 | 80-90 | 60-70 |
Märkus. Palun kinnitage meiega, kui teil on erinõudeid. |